Super pèmanan bonjan samaryom Cobalt SmCo leman 
Deskripsyon nan Super pèmanan Strong Samarium Cobalt SmCo leman
Pèmanan fò Samarium Cobalt leman yo te fè nan Sintered SmCo Magnet, Samaryom-Cobalt, 35% Sm, 60% Ko ak balans la yo te Fe & Cu.
Gen de konpozisyon nan leman nan fanmi sa a: Sm1Co5 ak Sm2Co17. Pi wo pwodwi enèji ki disponib nan Sm2Co17 yo nan seri 30MGOe a.
1: 5 materyèl alyaj
1: 5 ofri 16 MGOe (pwodwi enèji) nan 22 MGOe ak se te fè leve apeprè 50% samaryom ak 50% Cobalt. Seri 1: 5 gen yon maksimòm tanperati rekòmande ki rekòmande nan 250 ° C. SmCo 1: 5 leman mande pou pi ba fòs jaden pase 2:17 materyèl yo magnetize. Nan kèk sikonstans, 1: 5 materyèl yo ka mayetre avèk poto miltip, bay yon aparèy ki gen ladann ki disponib.
2:17 materyèl alyaj
2:17 ofri 24 MGOe 32 MGOe ak konpoze de apeprè 25% samaryom, 5% kwiv, 18% fè, 2% hafnium oswa zirkonyòm, ak rès la yo te kobalt. Seri a 2:17 nan gen yon tanperati opere maksimòm de 350 ° C. Klas espesyal nan 2:17 yo disponib ki ka opere menm tanperati ki pi wo. SmCo 2:17 egzije ekstrèmman gwo magazen jaden, ak mouvman polè miltip pa posib.
Samaryom Cobalt (SmCo) leman yo se leman pwisan leman latè ra ki konpoze de samaryom ak Cobalt. Yo souvan yo itilize nan motè pèfòmans segondè, moule ak mayetik séparation. Sa yo se leman frajil epi yo gen tandans fann ak chip. Samarium leman ka itilize pou aplikasyon pou tanperati wo kote neyodim pa pral travay.
Karakteristik nan Super pèmanan Strong Samarium Cobalt SmCo leman
• Samaryom cobalt leman yo difisil ak frajil epi yo ka chip oswa kraze si tonbe.
• Yo gen gwo pwopriyete mayetik.
• Samaryom cobalt leman ofri bon estabilite tèmik.
• Samaryom cobalt leman yo rezistan a korozyon.
• Samaryom cobalt leman rezistan nan demagnetization.
Super pèmanan Strong Samarium Cobalt SmCo Magnet s Range Size:
Samarium Cobalt Magnet Klas SmCo 5 (Sintered SmCo Magnet) 
Samaryom Cobalt Magnet Klas de SmCo 17 (Sintered SmCo Magnet)
Pwosesis nan Super pèmanan Strong Samarium Cobalt SmCo leman 
Karakteristik Fizik nan Super Pèmanan Strong Samarium Cobalt SmCo leman
Sintered Smco fizik karakteristik | |||
Non Paramèt | Inite | SmCo 1: 5 | SmCo 2:17 |
Dansite | G / cm3 | 8.3 | 8.4 |
Curie Tanperati Tc | K | 1000 | 1100 |
Vickers dite Hv | MPa | 450-500 | 550-600 |
Fòs konpresiv | MPa | 1000 | 800 |
Elektrik Rezistivite ρ | Ω.cm | 5 ~ 6 × 10-5 | 8 ~ 9 × 10-5 |
Koube fòs | Mpa | 150-180 | 130-150 |
Fòs rupture | Mpa | 400 | 350 |
Koefisyan ekspansyon tèmik | (10-6 / ℃) | 6⊥12 | 8plis11 |
Mayetik jaden fòs H (min) nan Super pèmanan Strong Samarium Cobalt SmCo leman
Materyèl | SmCo1: 5 | SmCo1: 5 | SmCo2: 17 | SmCo2: 17 | Ce (ko, Fe, cu) 5 |
Hcj Dimansyon | HCj ≥1194 | HCJ ≤ 1433 | HCJ ≥ 1433 | HCj ≤1273 | HCj ≤800 |
D emagnetizing koub SmCo5 ak Sm2Co17 samaryom Cobalt SmCo leman : 
Diferans ant Neyodim ak SmCo leman:
Konparezon nan NdFeB ak SmCo leman | ||
Pwopriyete | Neyodim | SmCo |
Remanans (T) | 1-1.3 | 0.82-1.16 |
Koerivite (MA / m) | 0.875-1.99 | 0.493-1.59 |
Relatif pèmeyabilite | 1.05 | 1.05 |
Tanperati koyefisyan nan remanans (% / K) | -0.12 | -0.03 |
Tanperati koyefisyan nan coercivity (% / K) | -0.55 ..- 0.65 | -0.15 ..- 0.30 |
Curie tanperati (° C) | 320 | 800 |
Dansite (g / cm3) | 7.3-7.5 | 8.2-8.4 |
CTE, direksyon mayetik (1 / K) | 5.2 × 10-6 | 5.2 × 10-6 |
CTE, nòmal nan mayetik direksyon (1 / K) | -0.8 × 10-6 | 11 × 10-6 |
Fòs fleksib (N / mm2) | 250 | 150 |
Konpresiv fòs (N / mm2) | 1100 | 800 |
Fòs rupture (N / mm2) | 75 | 35 |
Vickers dite (HV) | 550-650 | 500-650 |
Elektrik rezistivite (Ω · cm) | (110-170) × 10-6 | 86 × 10-6 |